Synthesis and Enhancement of mechanical properties of TiO2 Nano particles on Mild steel

Kumar K. Santhosh1, Priyanka Narlagiri2,*

1Asst. Professor, Department of Mechanical Engineering, S R Engineering College, Warangal, Telangana. India. santhunitt@gmail.com

2PG Student, Department of Mechanical Engineering, S R Engineering College, Warangal, Telangana. India

*Corresponding Author E-mail: priya.narlagiri@gmail.com

Abstract

In this project we have found that the XRD pattern of the TiO2 nano particles, the peaks are observed at corresponding values. The SEM images of TiO2 nano particles shows respectable morphology and Grain size of TiO2 nano particles were nearly 60.03 nm. The Energy dispersive X-ray spectroscopy reveals that the required phase has present. Titanium and oxygen (O) Elements are present in the sample. The grain structure and size were nearly 240 nm. TiO2 Coated nano particles on mild steel at 500° C, shows respectable morphology when compared with base metal of the sample and grain size of coated sample 500° C were nearly 204 nm. Initially the surface roughness of the base metal is high when compared with heat treated sample at 500°C due to the heat treatment the surface roughness of the sample is smooth. Surface roughness is high after deposition of TiO2 nano particles on mild steel at 500°C, due to high bond generated between TiO2 and mild steel during dipping process.

Top

Keywords

TiO2 nano particles, mild steel, XRD and SEM analysis.

Top

  
║ Site map ║ Privacy Policy ║ Copyright ║ Terms & Conditions ║ Page Rank Tool
567,068,513 visitor(s) since 30th May, 2005.
All rights reserved. Site designed and maintained by DIVA ENTERPRISES PVT. LTD..
Note: Please use Internet Explorer (6.0 or above). Some functionalities may not work in other browsers.